Title: Microstructural characterisation and thermal stability of an Mg-Al-Sr alloy prepared by rheo-diecasting
Authors: Wang, Y
Liu, G
Wang, F
Fan, Z
Keywords: Microstructural characterisation; thermal stability; Mg-Al-Sr (AJ62) alloy; rheo-diecasting
Publication Date: 2007
Publisher: University of Sheffield
Citation: Proceedings of the 5th Decennial International Conference on Solidification Processings, Sheffield, July 2007. pp. 600-605.
Abstract: A commercial Mg-6Al-2Sr (AJ62) alloy has been prepared by a semisolid rheo-diecasting (RDC) process. The microstructure of the RDC alloy exhibits typical semisolid solidification features, i.e., 8.4 vol% primary α-Mg globules (23 μm in diameter), formed in the slurry maker at the primary solidification stage, uniformly distributed in the matrix of fine α-Mg grain size (8.2 μm) and intergranular eutectic Al4Sr lamellae, which resulted from secondary solidification inside the die. A ternary Mg-Al-Sr phase was also observed. Heat treatment revealed the extreme thermal stability of the RDC AJ62 alloy. The hardness showed little change up to 12 hours at 450°C, whilst the Al4Sr eutectic lamellae were broken up, spheroidised and coarsened during the annealing. The RDC alloy offers superior mechanical properties, especially ductility, over the same alloy produced by high pressure die-casting.
URI: http://bura.brunel.ac.uk/handle/2438/2682
Appears in Collections:Materials Engineering
Brunel Centre for Advanced Solidification Technology (BCAST)

Files in This Item:

File Description SizeFormat
18-sp07-2.pdf3.91 MBAdobe PDFView/Open

Items in BURA are protected by copyright, with all rights reserved, unless otherwise indicated.

 


Library (c) Brunel University.    Powered By: DSpace
Send us your
Feedback. Last Updated: September 14, 2010.
Managed by:
Hassan Bhuiyan