Effect of sintering temperature and heat treatment on electrical properties of indium oxide based ceramics

Abstract

Indium oxide based ceramics with bismuth oxide addition were sintered in air in the temperature range 800-1300 ºC. Current-voltage characteristics of In2O3-Bi2O3 ceramics sintered at different temperatures are weakly nonlinear. After an additional heat treatment in air at about 200 ºC samples sintered at a temperature within the narrow range of about 1050-1100 ºC exhibit a current-limiting effect accompanied by low-frequency current oscillations. It is shown that the observed electrical properties are controlled by the grain-boundary barriers and the heat treatment in air at 200 ºC leads to the decrease in the barrier height. Electrical measurements, scanning electron microscopy and X-ray photoelectron spectroscopy results suggest that the current-limiting effect observed in In2O3-Bi2O3 can be explained in terms of the modified barrier model proposed earlier for the explanation of similar effect in In2O3-SrO ceramics.