https://bura.brunel.ac.uk/handle/2438/33809| Title: | Analyzing the Effect of Fe on the Microstructure and Mechanical Properties of a Fibrous AA6110 Alloy |
| Authors: | Sadeghi, Fazlollah Barekar, Nilam Subroto, Tungky Shurkin, Pavel Scamans, Geoff Barbatti, Carla |
| Keywords: | Al alloys;texture;dynamic recrystallization;fibre texture;Fe-based intermetallics |
| Issue Date: | 24-Aug-2026 |
| Publisher: | Springer Nature |
| Citation: | Sadeghi, F. et al. 'Analyzing the Effect of Fe on the Microstructure and Mechanical Properties of a Fibrous AA6110 Alloy', Metals and Materials International, 0(ahead of print), pp. 1–17. doi: 10.1007/s12540-025-02211-3. |
| Abstract: | In this study, the effect of three different levels of iron impurity on the grain structure and texture of a fibrous AA6110 alloy after hot extrusion was investigated. Microstructural examination was carried out to measure the microtexture and the results were correlated with tensile and bending mechanical properties. Results demonstrated that the fragmented intermetallic particles after extrusion stimulate the nucleation of new grains, therefore refining the grain structure. The thickness of peripheral coarse grains was found to decrease by increasing Fe content due to increasing nano-sized dispersoid precipitation density. Increment Fe-rich intermetallics on the one hand leads to entrapment of Si solute reducing free Si needed for precipitation hardening shown via thermodynamic calculations. The bending formability was found to correlate with the grain structure of the PCG thickness. The results are compared with Part 1 of this research on the study of Fe content in recrystallized alloys. This work helps to a better understanding of recyclability in Al extrusion alloys. Graphical Abstract This shows the extruded AA6110 alloy having fibrous grain structures. The deep microstructural observation from macro to nanosized particles show the grain structure, particle stimulated nucleation, and dispersoid precipitation. Additional Fe in the composition of alloys result in increment of Fe-based intermetallic phase which break down and stretch during extrusion while grain structure evolves by dynamic recrystallization. |
| Description: | Data Availability: Data is available upon a reasonable request from the corresponding author. |
| URI: | https://bura.brunel.ac.uk/handle/2438/33809 |
| DOI: | https://doi.org/10.1007/s12540-025-02211-3 |
| ISSN: | 1598-9623 |
| Appears in Collections: | Brunel Centre for Advanced Solidification Technology (BCAST) |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| FullText.pdf | Copyright © The Author(s) 2026. Rights and permissions: Open Access. This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/. | 5.03 MB | Adobe PDF | View/Open |
This item is licensed under a Creative Commons License